FlameShield Nano Coat -

Slide

FlameShield Nano Coat

YNT-ZR-001

With modern living and manufacturing advancing, flame-retardant coatings are expected not only to protect substrates effectively but also to preserve their physical and mechanical properties.
Iridium Technology’s transparent flame-retardant coating draws inspiration from volcanic self-protection mechanisms, uniquely combining nano metal oxides with specialized flame-retardant polymers to ensure stable performance against fire and corrosion, safeguarding both materials and people.

Slide

Core Functions & Advantages

Slide

Superior Flame Retardant Protection
● Fire performance reaches the highest coating-grade standard: B1 (the coating does not continue burning or spread rapidly when exposed to open flame)
● Fire resistance up to 3 hours, preventing flame penetration

Eco-Friendly & Weather-Resistant
● Non-toxic and safe, producing no smoke or harmful gases during combustion
● Excellent weather resistance with high corrosion protection, suitable for various complex environments to ensure long-term stable protection
● Transparent, single-component coating; surface-dry in 10 minutes, fully cured in 30 minutes, quickly forming a fire barrier on the substrate

Slide

Applications

Slide

Where to Use

Suitable for wooden substrates

How to Apply

Pre-treat substrate to ensure a clean, dry surface; apply by brushing or spraying

Slide

Performance & Testing

Test Item	Standard	Result
Limiting Oxygen Index	GB/T 2406.2-2009	28.9% on PU foam substrate
Flame Retardant Rating	GB/T2408-2008	B1
6M HCl Resistance, 3200 h	GB/T 9274-1988	No change in film
6M NaOH Resistance, 1500 h	GB/T 9274-1988	No change in film
Neutral Salt Spray Corrosion, 3000 h	GB/T 10125-1997	No change in film
Artificial Weathering Resistance, 8000 h	GB/T 1865-2009	No change in film
Impact Strength	GB/T 1732-1993	65 Kg·cm
Carbonization Height	In-House Test	1.8
Fire Resistance Limit	In-House Test	180 min
Film Thickness	In-House Test	200 μm
Coating Coverage	In-House Test	20–25 m²/L